Investigation of grafting silane coupling agents on superhydrophobicity of carbonyl iron/SiO2 particles for efficient oil/water mixture and emulsion separation

Scientific Reports volume 13, Article number: 788 (2023) Cite this article

1243 Accesses

5 Citations

5 Altmetric

Metrics details

The present study demonstrated the wettability properties of grafting silane coupling agents on carbonyl iron (CI)/SiO2 particles for efficient oil/water mixture and emulsion separation. CI particles were first reacted with Tetraethoxysilane (TEOS) to create a magnetic component. Then, CI/SiO2 particles were altered by 1H,1H,2H,2H-perfluorodecyltriethoxysilane (FAS) and Hexamethyldisilazane (HDMS) to create magnetic superhydrophobic/superoleophilic, recyclable, and reusable sorbent powders. The water contact angle (WCA) values of the as-prepared particles, CI, CI/SiO2, CI/SiO2@FAS, and CI/SiO2@HMDS, were 5.4° ± 1.3°, 6.4° ± 1.4°, 151.9° ± 2.1°, and 170.1° ± 1.1°, respectively. In addition, the oil contact angles (OCAs) of a variety of oils were found to be equivalent to 0°. Hence, superhydrophobic/superoleophilic particles for kind of different oils were shown sorption capacities of 1.7–3.1 g/g and 2.5–4.3 g/g for CI/SiO2@FAS, and CI/SiO2@HMDS, respectively. Besides, for 1%w/w hexane/water emulsion separation efficiency higher than 99%, the lowest mass was obtained at 50 and 200 mg for CI/SiO2@HDMS and CI/SiO2@HDMS, respectively, suggesting a new effective material for separating tiny oil droplets. Also, the reusability and chemical durability of the superhydrophobic samples made them a prime candidate for use in different harsh conditions.

In today’s world, the amount of wastewater produced is increasing dramatically due to the development of various industrious and booming populations globally1,2,3,4. Industrial wastewater discharge and oil spills in the marine environment not only threaten ecosystems and human health but also destroy a wide range of Earth's natural resources, which motivates researchers to develop proactive, drastic, and solution-focused strategies to mitigate these serious environmental issues5,6,7. So far, numerous materials with various properties have been produced for oil and water separation. Synthesized materials for separation should have the requisite surface qualities such as high surface area, high wettability or superhydrophobicity, good durability, and so on8,9,10,11,12,13.

Wetting and anti-wetting properties of solid surfaces are one of the most common natural phenomena that we see widely in the environment just like dew on plants or the water droplets on some species of insects’ wings that artificial type for the first time was introduced as super-anti wetting property by Ollivier14. A Superhydrophobic surface with a high apparent contact angle (> 150°) is commonly used in the form of mesh and porous materials for oil and water separations15. These materials suffer from some drawbacks including time-consuming synthesis processes, high cost, and low efficiency, that are considered obstacles to their industrial applications9,16,17,18,19. Hence, developing simple, scalable, and low-cost fabrication methods is of great importance for the commercial scale of separation projects9. The majority of conducted investigations on the hydrophobicity issues have concerned the fabrication methods and processes, the theories behind the unique wettability and non-wettability as well as their applications14.

Various methods and strategies have been introduced to fabricate different materials with excellent superhydrophobicity, such as chemical vapor deposition20, phase separation21, layer-by-layer assembly, electrospinning deposition22, colloid assembly23, chemical etching24, etc.25,26. In terms of the mechanism, silanes that do not have hydrolyzable groups, such as Si-CI, Si-OCH3, Si-OCH2CH3, and Si-NH-Si, react with water to create silanols, which are then coupled to hydroxyl groups on the surface of materials. Some of the most important factors that should be considered for the production and modification of superhydrophobic materials include surface roughness and low surface energy of materials25. Organic materials with superhydrophobicity typically are in the form of powder or 3D porous sponges to separate water and oil27. Also, they can be produced as porous flat films or coated on the meshes28. Stainless steel (SS) and copper material, the most common metallic mesh substrates, can be modified to become superhydrophobic adsorbents15. Hierarchical micro and nano roughness surfaces are fabricated by different methods such as acid erosion, colloidal assembly, rough polymer film, crystal growth, and chemical vapor deposition (CVD)15,29,30,31. Currently, alkylsilanes or perfluoroalkylsilanes, PDMS-based polymers, thiols, long alkyl chain fatty acids, perfluorinated polymers, and so on are used for decreasing surface energy. For example, chlorosilanes such as 1H, 1H, 2H, 2H-perfluoroctyldimethylchlorosilane (PFODMCS), dimethyldichlorosilane (DMDCS), and 1H, 1H, 2H, 2Hperfluorooctyltrichlorosilane (PFOTCS) can easily give surfaces the superhydrophobic property14,32.

Matin et al. reported the dip-coating of SS separator using different concentrations of silane materials, perfluo-rooctyltrichlorosilane33. They demonstrated that after seven cycles, water droplets on the superhydrophobic surface of the SS reached an angle of about 150.5°, and the resulting superhydrophobic adsorbent successfully separated the various types of oils with a 95% efficiency. Qiang et al. reported the fabrication of silane functionalized reduced Graphene oxide nanoribbons (GONR) coated polyurethane (PU) sponge composites via a facile dip-coating method. The produced porous superhydrophobic composite has good oil/water separation selectivity and capacity with high efficiency (> 97% after 10 cycles) and water contact angles of higher than 150°34. Khodaei et al. developed superhydrophobic aluminum with a nano/micro hierarchical surface structure by chemical etching and decorating nanoparticles with a silane-based nanocomposite coating (Al2O3 nanoparticles integrated TEOSGPTMS)35. Wang et al. demonstrated the easy production of superhydrophobic and superoleophobic cotton textiles modified with polysiloxane nanowires for oil/water separation. The low-surface-energy polysiloxane nanowires besides the hierarchical structure led to the cotton fabrics with great superhydrophobicity (WCAs 163°) and excellent stability36.

In this work, carbonyl iron particles were first reacted with Tetraethoxysilane, and then the surface was altered by FAS and HDMS in order to create superhydrophobic/superoleophilic and recyclable adsorbent particles. The characterization of the carbonyl iron modification particles with various silane groups was evaluated by using FT-IR, XRD, and VSM. The WCA study was then completed to quantitatively assess the particles' superhydrophobicity. The sorption capacity of superhydrophobic particles was also examined for oil/water separation and emulsion mixture under various circumstances.

Absolute ethanol and Ammonia (25–28%wt.) were bought from DR-MOJALALI Medicines Co., Ltd, and Carbonyl Iron (CI) particles from BASF Company, Germany. Tetraethoxysilane (TEOS, 99.9%), Hexamethyldisilazane (HMDS, 98%) and 1H,1H,2H,2H-perfluorodecyltriethoxysilane (PFDTES or FAS, 97%) were bought from Sigma-Aldrich. All of the chemical reagents were utilized exactly as they were received, with no further purification.

First, 0.2 g of carbonyl iron was added into 40 mL of ethanol which contained 4 mL of ammonia solution. Subsequently, 0.2 mL of TEOS was added and sonicated in a sonication bath for 6 h. The solution was then three times vacuum-washed with ethanol in the following step. After that, it spent 24 h in an oven at 110 °C. Then, carbonyl iron particles were coated with SiO2(CI/SiO2).

First, 60 mL of ethanol containing 6 mL of an ammonia solution was mixed with 0.2 g of CI/SiO2. After that, 0.4 mL of FAS was added, and it was sonicated for 8 h in a sonication bath. The solution was then three times vacuum-washed with ethanol in the following step. After that, it spent 24 h in an oven at 110 °C. After this period of time, carbonyl iron particles were given a coating of SiO2-FAS, denoted by the notation CI/SiO2@FAS.

First, 0.2 g of CI/SiO2 was mixed with 100 mL of ethanol and 8 mL of an ammonia solution. After that, 1 mL of HMDS was added, and the mixture was sonicated for 4 h in a sonication bath. The solution was then three times vacuum-washed with ethanol in the following step. After that, it spent 24 h in an oven at 110 °C. After this time, carbonyl iron particles were coated with SiO2-HMDS(CI/SiO2@HMDS).

Fourier transform infrared spectroscopy was used to examine the functional groups on the surface of carbonyl iron particles (FT-IR, THERMO, AVATAR). The crystal structure of carbonyl iron particles modified with different silane groups was investigated by analysis of the X-ray diffraction (XRD, Philips, PW1730). The magnetic properties of the modified particles were also measured using a vibrating sample magnetometer (VSM, Model No. 155, Magnet: Varian, V-7300). Furthermore, Jikan CAG-20, Jikan Co., and Image J® 1.51i software investigated the oil and water contact angle of altered particles.

Oil and water were emulsified at 1% by weight in hexane. In this regard, to create a stable emulsion, one gram of oil was dissolved in 99 g of deionized water and swirled for 30 min. An ultrasonic probe (100 kW) was used for 10 min to minimize the size of oil droplets in water. It should be noted that stirring for longer periods caused the formation of nano-sized droplets. As a result, the oil–water emulsion was made by adding various oil concentrations to the water's surface, ranging from 0.1 to 1 mL. In addition, one mL of oil was added to the water's surface to create the oil–water mixture. The same method was used to make mixtures and emulsions of water with kerosene, silicon oil, and gasoline.

The efficacy and capability of modified materials were demonstrated using their sorption capacity. The following equation (Eq. (1)) can be used to determine the water or oil sorption capacity from the measurement of the weight of the liquid that is adsorbed due to placement or immersion:

While me and m0 are the material's weight before and after liquid sorption, respectively, and Q (g/g) is the amount of sorption capacity for various mixtures and emulsions, the oil separation's sorption capacity was estimated.

Magnetic recycling of modified carbonyl iron particles has been investigated. Following oil adsorption, the superhydrophobic magnetic particles are collected, treated with chloroform and ethanol, and dried for 12 h at 60 °C. These particles will subsequently be employed in the oil sorption technique that follows. The reusability of hydrophobic magnetic particles was investigated over ten cycles.

The reaction mechanism of different silane agents on the carbonyl iron particles has been shown in Fig. 1. The TEOS was hydrolyzed in the presence of ethanol and water, and Si–OR + H2O was converted to Si–OH + ROH. Then the silica network (Si–O–Si) was created through a condensation reaction on the surface of carbonyl iron particles according to Fig. 1a. FAS was then formed on the surface of carbonyl iron-SiO2 via a hydrolysis and condensation process (Fig. 1b). Similarly, as can be seen in Fig. 1c, the HDMS was hydrolyzed and condensed on the surface of carbonyl iron-SiO2. In addition, due to the sensitivity of conversion rates to the presence of acids and bases, ammonia solution was employed as a catalyst for all processes1,2,37,38,39,40.

Mechanism of carbonyl iron reaction with (a) SiO2, (b) SiO2@FAS, and (c) SiO2@HDMS.

Functional groups have been examined using FT-IR analysis to confirm that iron carbonyl particles react with various silane groups. Figure 2 shows peaks related to different functional groups of SI, FAS, and HDMS on the surface of iron carbonyl particles. The spectra of CI particles modified with SiO2, FAS, and HDMS showed patterns typical of siloxane materials. The peaks of several silane groups, including Si–O–C, Si–O–Si, and Si–O–C, were assigned to a range of 1000 to 2000 cm−138,41. On the FT-IR curve, the peak relative to Si–O–Fe was given 500 cm−1. Also, at 845 and 1255 cm−1, FT-IR signals linked with Si–C were found37. The wide band about 3500 cm−1 shows the stretching of several OH groups; this peak was gotten weaker by adding HDMS and FAS to the surface of CI/SiO2, indicating that the OH groups had been replaced by silane bands40,42,43,44.

FTIR of carbonyl iron and modified hydrophobic particles with SiO2, SiO2@FAS, and SiO2@HDMS.

XRD analysis was used to investigate oxidation or changes in the crystal structure that occur during synthesis. The XRD pattern for iron carbonyl particles modified with SiO2, SiO2@FAS, and SiO2@HDMS is shown in the Fig. 3. Then, the resulting XRD pattern revealed the 2θ of 44° given to (110), and 66° to (211) connected to the Fe peaks in the synthesized sample. No additional peak has been seen for any alterations other than these two peaks, proving that the oxidation reaction was not performed throughout the synthesis process1.

XRD of carbonyl iron and modified hydrophobic particles with SiO2, SiO2@FAS, and SiO2@HDMS.

The magnetic characteristics of carbonyl iron particles with various silane coupling agents were studied using a VSM and the results are depicted in Fig. 4. In the 10 kOe field, it was shown that carbonyl particles had strong magnetic permeability with magnetic saturation of 210, 188, 167, and 166 emu/g for bare CI, CI/SiO2, CI/SiO2@FAS, and CI/SiO2@HDMS, respectively. The modified particles still exhibit high saturation magnetism despite having a non-magnetic covering. In addition, the magnetization curve shows only a small amount of magnetic hysteresis as well as coercivity (Hc) and remnant magnetism (Mr) for modified carbonyl iron particles. Other magnetic properties of samples, Hc and Mr, are summarized in Table 1.

VSM curve for modified hydrophobic particles (a) bare CI, (b) SiO2, (c) SiO2@FAS, and (d) SiO2@HDMS.

One of the most crucial factors to consider when assessing a material's wettability characteristics is the water contact angle (WCA) or oil contact angle (OCA). Hence, the sessile water droplet method with a volume of 5 µL was utilized so that the wettability of particles (CI, CI/SiO2, CI/SiO2@FAS, and CI/SiO2@HMDS) could be evaluated. The powder particles were compacted between two glass substrates to form a level layer. Utilizing a Hamilton microliter syringe, vertical liquid droplets were put on the accumulated particles. Five contact angle measurements were carried out in various places, and the findings were provided according to their mean value. Image J® 1.51i software was used to process all liquid droplet photographs45.

Figure 5 depicts the digital photographs and the WCA variation of the liquid droplets on the stacked particles. According to the findings, the WCA values for CI, CI/SiO2, CI/SiO2@FAS, and CI/SiO2@HMDS were 5.4° ± 1.3°, 6.4° ± 1.4°, 151.9° ± 2.1°, and 170.1° ± 1.1°, respectively. In addition, it is essential to point out that the OCAs of a variety of oils were found to be equivalent to 0°. The findings demonstrate that both CI and CI/SiO2 possess superhydrophilicity and superoleophilicity. Because of this, the use of these materials in processes that separate oil and water cannot be considered a viable option. On the other hand, CI/SiO2@FAS and CI/SiO2@HMDS exhibited features of superhydrophobicity and superoleophilicity properties. The production of a high water-repellent substrate is specifically dependent on two primary factors: high surface roughness and the use of material with low surface energy. The different processes of hydrolysis and condensation that take place on the sample's surface lead the materials to behave differently in terms of their propensity to adsorb water46,47.

(a) The digital photos and (b) WCA variation of water droplets on the layered particles.

Due to their unique superhydrophobicity/superoleophilicity qualities, CI/SiO2@FAS and CI/SiO2@HMDS can be considered very effective adsorbents in oil/water mixtures and emulsion separations. In addition, the ferromagnetic responses of particles can contribute to the collection and reuse processes. For the separation of oils from the oil/water mixture in the batch system, the as-prepared modified particles were used. Initially, 300 mg of red-dyed oil was sprinkled onto the water's surface. Subsequently, the magnetic particles were left on the oil spill for 5 min, and time was given. The patch of slick oil began to reduce at that point.

Over time, it was discovered that superhydrophobic/superoleophilic powders intuitively capture and cover oil droplets before sinking into the water. After collecting the oil-particle combination with a magnet, the ultimate mass of the marble was calculated. The measured sorption capacity for oils, including hexane, kerosene, silicone oil, and gasoline, were in the ranges of 1.7–3.1 g/g and 2.5–4.3 g/g for CI/SiO2@FAS, and CI/SiO2@HMDS, respectively (Fig. 6), which can compete with other used absorbents (Table 2). The results showed that the highest and lowest sorption capacity belonged to hexane and silicone oil, respectively.

The sorption capacity of CI/SiO2@FAS, and CI/SiO2@HMDS.

In the recent decade, numerous studies have been done to address oil/water emulsion separation. Foams, metal meshes, and fabric materials are some technologies that can be used to separate oil from oil emulsions in water; however, these approaches all have their drawbacks59,60,61,62. In this context, using particles that are both superhydrophobic and superoleophilic can be an effective strategy for separating oil and water emulsions. In the current investigation, a number of 1%w/w oil/water emulsions were created. These emulsions included hexane, kerosene, silicone oil, and gasoline. The size distributions of oil droplets in different surfactant-free oil/water emulsions were shown in Fig. 7. Hexane, kerosene, silicone oil, and gasoline all had an average droplet size of 6.54 ± 1.78, 8.32 ± 1.54, 13.49 ± 6.94, and 6.12 ± 2.40 µm, respectively, when they were homogeneously distributed in the water. It is important to highlight that the images obtained from optical microscopy demonstrated that the emulsions kept their stability over one day. Particles ranging in mass from 5 to 250 mg were added directly to 3 mL of emulsions and vigorously vortexed for 10 min. The upper aqueous solution was removed after the oily particles were separated from the water using a magnetic field to evaluate the water profile. A schematic illustration of the separation of tiny oil droplets from the oil-in-water emulsion is illustrated in Fig. 8a. Initially, a low dosage of superhydrophobic/superoleophilic particles cannot separate oil droplets totally and the final solution looks turbid. By increasing the mass of sorbent in the system, the final solution becomes transparent, which is different for each sorbent and oil (Fig. 8b). For instance, by adding 50 mg of CI/SiO2@FAS particles to 1%w/w hexane/water emulsion, the resultant final filtrate solution was semitransparent. In contrast, by adding the same mass of CI/SiO2@HDMS, the final solution can become transparent. The lowest mass of particles to separate a 1%w/w hexane/water emulsion was 50 and 200 mg for CI/SiO2@HDMS and CI/SiO2@HDMS, respectively. As a result, the powdery materials such as CI/SiO2@HDMS and CI/SiO2@HDMS particles have the ability to contact directly with emulsion droplets, which can be suggested as very effective systems in separating oil droplets from oil-in-water emulsions.

Oil droplet size distributions of various surfactant-free oil/water emulsions; (a) hexane, (b) silicone oil, (c) gasoline, and (d) kerosene.

(a) Schematic illustration of separation of tiny oil-droplets from the oil-in-water emulsion, (b) the effect of sorbent mass on the turbidity or transparency of final filtrate solution from the hexane-in-water emulsion.

The sorption capacities of recyclable superhydrophobic/superoleophilic CI/SiO2@HDMS particles for oils are presented in Fig. 9a, which indicates that the sorption capacity has not significantly changed even after 10 separation cycles. For instance, the sorption capacity of hexane revealed that after ten cycles, the original sorption capacity was reduced by just 0.8 g/g (4.3 to 3.5 g/g), which is a relatively small amount. The shift in WCAs is responsible for the fluctuating sorption capacities, as this has been demonstrated. Figure 9b displays a slight decreasing trend in the water contact angles (WCA) of the droplets on the regenerated particles, which is consistent with the sorption capacity data. As shown in Fig. 9c, the as-prepared particles can meet practical needs in severe and hard settings since their sorption capacity for oils remains roughly constant even in acidic, alkaline, and high-saline environments. Wetting behavior and chemical stability under a wide range of circumstances is the main problem with superhydrophobic/superoleophilic surfaces (acidic, alkaline, and saline solution). WCA variations were also used to examine the effects of varying the pH of the prepared superhydrophobic/superoleophilic particles for a week. Good hydrophobicity is indicated by WCA values of more than 145°, as seen in Fig. 9d. Superhydrophobic samples are shown to have outstanding chemical durability and physical stability in steady or flowing settings, making them a prime candidate for oil/water separation technology.

(a) Recyclability of the CI/SiO2@HDMS in different regeneration cycles, (b) water contact angle variations in different cycles, (c) the performance of CI/SiO2@HDMS for sorption oils under various circumstances, and (d) water contact angle variations for immersion at different pH values for one week.

In conclusion, the superparamagnetic superhydrophobic/superoleophilic, as well as reusable and durable carbonyl iron/SiO2 particles were prepared through a simple grafting route. Silane coupling agents, namely 1H,1H,2H,2H-perfluorodecyltriethoxysilane (FAS) and Hexamethyldisilazane (HDMS), were used to illustrate the effect of modifying surface wettability of the resulted samples. The reaction mechanism of different silane agents on the carbonyl iron particles has shown that FAS and HDMS were formed on the surface of carbonyl iron-SiO2 via a hydrolysis and condensation process via the creation of a silica network. CI/SiO2@FAS and CI/SiO2@HMDS exhibited ferromagnetic properties with magnetic saturation of 167 and 166 emu/g for CI/SiO2@FAS and CI/SiO2@HDMS, respectively. Also, the measured sorption capacities of CI/SiO2@FAS and CI/SiO2@HMDS were in the ranges of 1.7–3.1 g/g and 2.5–4.3 g/g for different kinds of oils, which can compete with other used absorbents. Also, the sorption capacities of recyclable superhydrophobic/superoleophilic particles indicated good recyclability and reusability even after ten separation cycles. Besides, superhydrophobic samples have outstanding chemical durability and physical stability in acidic, alkaline, and high-saline circumstances, making them a prime candidate for oil/water separation technology. Consequently, CI/SiO2@HDMS and CI/SiO2@HDMS particles have the ability to contact directly with emulsion droplets, which can be suggested as very effective systems in separating oil droplets from oil-in-water emulsions.

All data generated or analyzed data for the experimental part of this study are included in this published article. The data that support the findings of this study are available from the corresponding author, [Yahya Rabbani], upon reasonable request. Moreover, all other data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.

Rabbani, Y., Shariaty-Niassar, M. & Ebrahimi, S. A. S. The effect of superhydrophobicity of prickly shape carbonyl iron particles on the oil-water adsorption. Ceram. Int. 47, 28400–28410 (2021).

Article CAS Google Scholar

Rabbani, Y., Shariaty-Niassar, M. & Ebrahimi, S. A. S. The optimization effect of different parameters on the super hydrophobicity of prickly-shaped carbonyl iron particles. RSC Adv. 12, 12760–12772 (2022).

Article ADS CAS Google Scholar

Shayesteh, H., Norouzbeigi, R. & Rahbar-Kelishami, A. Hydrothermal facile fabrication of superhydrophobic magnetic nanospiky nickel wires: Optimization via statistical design. Surf. Interfaces 26, 101315 (2021).

Article CAS Google Scholar

Shayesteh, H., Rahbar-Kelishami, A. & Norouzbeigi, R. Superhydrophobic/superoleophilic micro/nanostructure nickel particles for oil/water mixture and emulsion separation. Ceram. Int. 48, 10999–11008 (2022).

Article CAS Google Scholar

He, X., Liu, Q. & Xu, Z. Treatment of oily wastewaters using magnetic Janus nanoparticles of asymmetric surface wettability. J. Colloid Interface Sci. 568, 207–220 (2020).

Article ADS CAS Google Scholar

Li, S. et al. Superhydrophobic-superoleophilic heptafluorodecyl triethoxysilane/graphitic carbon spheres Co-modified porous monolith for water/oil separation. Ceram. Int. 47, 25674–25679 (2021).

Article CAS Google Scholar

Cai, Y., Shi, S. Q., Fang, Z. & Li, J. Design, development, and outlook of superwettability membranes in oil/water emulsions separation. Adv. Mater. Interfaces 8, 2100799 (2021).

Article CAS Google Scholar

Cai, Y. et al. Durable, flexible, and super-hydrophobic wood membrane with nanopore by molecular cross-linking for efficient separation of stabilized water/oil emulsions. EcoMat 4, 1–14 (2022).

Article Google Scholar

Tang, X. et al. A facile procedure to modify filter paper for oil–water separation. RSC Adv. 7, 30495–30499 (2017).

Article ADS CAS Google Scholar

Fanaei, F., Moussavi, G. & Shekoohiyan, S. Enhanced treatment of the oil-contaminated soil using biosurfactant-assisted washing operation combined with H2O2-stimulated biotreatment of the effluent. J. Environ. Manag. 271, 110941 (2020).

Article CAS Google Scholar

Shokri, A. & Fard, M. S. A critical review in electrocoagulation technology applied for oil removal in industrial wastewater. Chemosphere 288, 132355 (2022).

Article ADS CAS Google Scholar

Ren, S., Ye, X. P. & Borole, A. P. Separation of chemical groups from bio-oil water-extract via sequential organic solvent extraction. J. Anal. Appl. Pyrolysis 123, 30–39 (2017).

Article CAS Google Scholar

Wu, J. et al. A 3D smart wood membrane with high flux and efficiency for separation of stabilized oil/water emulsions. J. Hazard. Mater. 441, 129900 (2023).

Article CAS Google Scholar

Li, L., Li, B., Dong, J. & Zhang, J. Roles of silanes and silicones in forming superhydrophobic and superoleophobic materials. J. Mater. Chem. A 4, 13677–13725 (2016).

Article CAS Google Scholar

Rasouli, S., Rezaei, N., Hamedi, H., Zendehboudi, S. & Duan, X. Design, fabrication, and characterization of a facile superhydrophobic and superoleophilic mesh-based membrane for selective oil-water separation. Chem. Eng. Sci. 236, 116354 (2021).

Article CAS Google Scholar

Ju, J. et al. A highly stretchable and robust non-fluorinated superhydrophobic surface. J. Mater. Chem. A 5, 16273–16280 (2017).

Article CAS Google Scholar

Panda, A., Varshney, P., Mohapatra, S. S. & Kumar, A. Development of liquid repellent coating on cotton fabric by simple binary silanization with excellent self-cleaning and oil-water separation properties. Carbohydr. Polym. 181, 1052–1060 (2018).

Article CAS Google Scholar

Rather, A. M., Jana, N., Begum, S., Srivastava, H. K. & Manna, U. Exceptional control on physical properties of a polymeric material through alcoholic solvent-mediated environment-friendly Michael addition reaction. Green Chem. 19, 4527–4532 (2017).

Article CAS Google Scholar

Cai, Y. et al. Thermo-controlled, self-released smart wood tailored by nanotechnology for fast clean-up of highly viscous liquids. SmartMat https://doi.org/10.1002/smm2.1133 (2022).

Article Google Scholar

Şakalak, H., Yılmaz, K., Gürsoy, M. & Karaman, M. Roll-to roll initiated chemical vapor deposition of super hydrophobic thin films on large-scale flexible substrates. Chem. Eng. Sci. 215, 115466 (2020).

Article Google Scholar

Molla-Abbasi, P. Effect of nano-size nodular structure induced by CNT-promoted phase separation on the fabrication of superhydrophobic polyvinyl chloride films. Polym. Adv. Technol. 32, 391–401 (2021).

Article CAS Google Scholar

Wang, Y. et al. Lightweight, flexible and superhydrophobic conductive composite films based on layer-by-layer self-assembly for high-performance electromagnetic interference shielding. Compos. Part A Appl. Sci. Manuf. 141, 106199 (2021).

Article CAS Google Scholar

Seyfert, C., Berenschot, E. J. W., Tas, N. R., Susarrey-Arce, A. & Marin, A. Evaporation-driven colloidal cluster assembly using droplets on superhydrophobic fractal-like structures. Soft Matter 17, 506–515 (2021).

Article ADS CAS Google Scholar

Wei, D. et al. Controllable superhydrophobic surfaces with tunable adhesion on Mg alloys by a simple etching method and its corrosion inhibition performance. Chem. Eng. J. 404, 126444 (2021).

Article CAS Google Scholar

Khan, M. Z., Baheti, V., Militky, J., Ali, A. & Vikova, M. Superhydrophobicity, UV protection and oil/water separation properties of fly ash/trimethoxy (octadecyl) silane coated cotton fabrics. Carbohydr. Polym. 202, 571–580 (2018).

Article CAS Google Scholar

Li, H., Yang, J., Li, P., Lan, T. & Peng, L. A facile method for preparation superhydrophobic paper with enhanced physical strength and moisture-proofing property. Carbohydr. Polym. 160, 9–17 (2017).

Article CAS Google Scholar

Cai, Y. et al. A polydimethylsiloxane-based sponge for water purification and interfacial solar steam generation. J. Colloid Interface Sci. 629, 895–907 (2023).

Article CAS Google Scholar

Xiong, X., Xie, F. & Meng, J. Preparation of superhydrophobic porous coating film with the matrix covered with polydimethylsiloxane for oil/water separation. Prog. Org. Coat. 125, 365–371 (2018).

Article CAS Google Scholar

Bashar, M. M., Zhu, H., Yamamoto, S. & Mitsuishi, M. Superhydrophobic surfaces with fluorinated cellulose nanofiber assemblies for oil–water separation. RSC Adv. 7, 37168–37174 (2017).

Article ADS CAS Google Scholar

Varshney, P., Nanda, D., Satapathy, M., Mohapatra, S. S. & Kumar, A. A facile modification of steel mesh for oil–water separation. New J. Chem. 41, 7463–7471 (2017).

Article CAS Google Scholar

Zhang, Y. et al. Facile fabrication of zinc oxide coated superhydrophobic and superoleophilic meshes for efficient oil/water separation. RSC Adv. 8, 35150–35156 (2018).

Article ADS CAS Google Scholar

Lee, J., Hwang, H. S., Koh, W.-G. & Park, I. Robust and superomniphobic core-shell SiO2@ poly (1H, 1H, 2H, 2H-heptadecafluorodecyl methacrylate-co-methyl methacrylate) coating materials synthesized by thiol lactam initiated radical polymerization. Prog. Org. Coat. 148, 105851 (2020).

Article CAS Google Scholar

Matin, A., Baig, U. & Gondal, M. A. Facile preparation of superwetting surfaces by dip-coating of silane for efficient separation of different types of oils from water. Process Saf. Environ. Prot. 134, 226–238 (2020).

Article CAS Google Scholar

Qiang, F. et al. Facile synthesis of super-hydrophobic, electrically conductive and mechanically flexible functionalized graphene nanoribbon/polyurethane sponge for efficient oil/water separation at static and dynamic states. Chem. Eng. J. 334, 2154–2166 (2018).

Article CAS Google Scholar

Khodaei, M. & Shadmani, S. Superhydrophobicity on aluminum through reactive-etching and TEOS/GPTMS/nano-Al2O3 silane-based nanocomposite coating. Surf. Coat. Technol. 374, 1078–1090 (2019).

Article CAS Google Scholar

Wang, B. et al. Facile fabrication of robust superhydrophobic cotton fabrics modified by polysiloxane nanowires for oil/water separation. J. Coat. Technol. Res. 15, 611–621 (2018).

Article Google Scholar

Chang, C.-C., Wu, Y.-T. & Cheng, L.-P. Preparation of HMDS-modified silica/polyacrylate hydrophobic hard coatings on PMMA substrates. J. Coat. Technol. Res. 13, 999–1007 (2016).

Article CAS Google Scholar

Cvek, M., Moucka, R., Sedlacik, M. & Pavlinek, V. Electromagnetic, magnetorheological and stability properties of polysiloxane elastomers based on silane–modified carbonyl iron particles with enhanced wettability. Smart Mater. Struct. 26, 105003 (2017).

Article ADS Google Scholar

Chen, D., Yu, M., Zhu, M., Qi, S. & Fu, J. Carbonyl iron powder surface modification of magnetorheological elastomers for vibration absorbing application. Smart Mater. Struct. 25, 115005 (2016).

Article ADS Google Scholar

Yongbao, F., Tai, Q., Jun, Z. & Chunying, S. Effects of silane coupling agent on microstructure and mechanical properties of EPDM/carbonyl iron microwave absorbing patch. J. Wuhan Univ. Technol. Sci. Ed. 21, 78–82 (2006).

Article Google Scholar

Sedlacik, M., Mrlik, M., Babayan, V. & Pavlínek, V. Magnetorheological elastomers with efficient electromagnetic shielding. Compos. Struct. 135, 199–204 (2016).

Article Google Scholar

Issa, A. A. & Luyt, A. S. Kinetics of alkoxysilanes and organoalkoxysilanes polymerization: A review. Polymers 11, 537 (2019).

Article Google Scholar

Ignatyev, I. S., Montejo, M. & González, J. J. L. Theoretical study of the mechanisms of the hydrolysis and condensation reactions of silicon and titanium alkoxides: Similarities and differences. Dalt. Trans. 39, 6967–6973 (2010).

Article CAS Google Scholar

Rabbani, Y., Shariaty-Niassar, M. & Seyyedebrahimi, S. A. An investigation of the effects of dopamine on the superhydrophobicity of carbonyl iron particles with stearic acid. Iran. J. Chem. Eng. 17, 49–59 (2020).

Google Scholar

Shayesteh, H., Norouzbeigi, R. & Rahbar-Kelishami, A. Evaluation of superhydrophobicity of chemical-resistant magnetic spiky nickel nanowires grafted with silane coupling agent for highly efficient oil/water separation. Surf. Interfaces 28, 101685 (2022).

Article CAS Google Scholar

Yaghoubidoust, F. & Salimi, E. Antibacterial and antiplatelet properties of octyltrichlorosilane-modified cotton fabrics. Fibers Polym. 20, 1375–1379 (2019).

Article CAS Google Scholar

Wang, C. et al. Influences of VTMS/SiO2 ratios on the contact angle and morphology of modified super-hydrophobic silicon dioxide material by vinyl trimethoxy silane. Results Phys. 10, 891–902 (2018).

Article ADS Google Scholar

Yang, N., Luo, Z. X., Chen, S. C., Wu, G. & Wang, Y. Z. Superhydrophobic magnetic hollow carbon microspheres with hierarchical micro/nano-structure for ultrafast and highly-efficient multitasking oil-water separation. Carbon N. Y. 174, 70–78 (2021).

Article CAS Google Scholar

Chen, L. et al. Microwave-assisted solvothermal synthesis of covalent organic frameworks (COFs) with stable superhydrophobicity for oil/water separation. Chem. Asian J. 15, 3421–3427 (2020).

Article ADS CAS Google Scholar

Zhu, Q., Tao, F. & Pan, Q. Fast and selective removal of oils from water surface via highly hydrophobic core-shell Fe2O3@C nanoparticles under magnetic field. ACS Appl. Mater. Interfaces 2, 3141–3146 (2010).

Article CAS Google Scholar

Liu, T. et al. Facile preparation of Fe3O4@C/Cu core-shell sub-micron materials for oil removal from water surface. Appl. Surf. Sci. 466, 483–489 (2019).

Article ADS CAS Google Scholar

Gao, M. L., Zhao, S. Y., Chen, Z. Y., Liu, L. & Han, Z. B. Superhydrophobic/superoleophilic MOF composites for oil-water separation. Inorg. Chem. 58, 2261–2264 (2019).

Article CAS Google Scholar

Sann, E. E., Pan, Y., Gao, Z., Zhan, S. & Xia, F. Highly hydrophobic ZIF-8 particles and application for oil-water separation. Sep. Purif. Technol. 206, 186–191 (2018).

Article CAS Google Scholar

Xu, L. P. et al. Papilla-like magnetic particles with hierarchical structure for oil removal from water. Chem. Commun. 49, 8752–8754 (2013).

Article CAS Google Scholar

Chen, H. J. et al. Anomalous dispersion of magnetic spiky particles for enhanced oil emulsions/water separation. Nanoscale 10, 1978–1986 (2018).

Article CAS Google Scholar

Sarkar, A. & Mahapatra, S. Novel hydrophobic vaterite particles for oil removal and recovery. J. Mater. Chem. A 2, 3808–3818 (2014).

Article CAS Google Scholar

Yang, C. et al. Anomalous dispersion of bioinspired flower-like microparticles for oil/water separation. Nanotechnology 31, 95712 (2020).

Article CAS Google Scholar

Duan, C. et al. Smart enrichment and facile separation of oil from emulsions and mixtures by superhydrophobic/superoleophilic particles. ACS Appl. Mater. Interfaces 7, 10475–10481 (2015).

Article CAS Google Scholar

Du, J. et al. Hard-and-soft integration strategy for preparation of exceptionally stable Zr(Hf)-UiO-66 via thiol-ene click chemistry. ACS Appl. Mater. Interfaces 12, 28576–28585 (2020).

Article CAS Google Scholar

Wang, Y., Zhao, S., Guo, Z., Huang, J. & Liu, W. Multi-layer superhydrophobic nickel foam (NF) composite for highly efficient water-in-oil emulsion separation. Colloids Surf. A Physicochem. Eng. Asp. 628, 127299 (2021).

Article CAS Google Scholar

Cheng, C., Wei, Z., Gu, J., Wu, Z. & Zhao, Y. Rational design of Janus nanofibrous membranes with novel under-oil superhydrophilic/superhydrophobic asymmetric wettability for water-in-diesel emulsion separation. J. Colloid Interface Sci. 606, 1563–1571 (2022).

Article ADS CAS Google Scholar

Daksa Ejeta, D. et al. Preparation of superhydrophobic and superoleophilic cotton-based material for extremely high flux water-in-oil emulsion separation. Chem. Eng. J. 402, 126289 (2020).

Article CAS Google Scholar

Download references

School of Chemical Engineering, College of Engineering, University of Tehran (UT), Tehran, Iran

Yahya Rabbani

School of Chemical, Petroleum and Gas Engineering, Iran University of Science and Technology (IUST), Tehran, Iran

Hadi Shayesteh

School of Mechanical Engineering, College of Engineering, University of Tehran (UT), Tehran, Iran

Nima Haghshenas

Nanotechnology Department, School of Advanced Technologies, Iran University of Science and Technology (IUST), Tehran, Iran

Mobin Safarzadeh Khosrowshahi

You can also search for this author in PubMed Google Scholar

Y.R.: methodology, conceptualization, experimental work, methodology, software, writing the original draft. H.S.: conceptualization, methodology, software, writing the original draft. N.H.: experimental work, methodology. M.S.K.: software, writing—review and editing.

Correspondence to Yahya Rabbani or Hadi Shayesteh.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Rabbani, Y., Shayesteh, H., Haghshenas, N. et al. Investigation of grafting silane coupling agents on superhydrophobicity of carbonyl iron/SiO2 particles for efficient oil/water mixture and emulsion separation. Sci Rep 13, 788 (2023). https://doi.org/10.1038/s41598-023-28131-z

Download citation

Received: 27 October 2022

Accepted: 13 January 2023

Published: 16 January 2023

DOI: https://doi.org/10.1038/s41598-023-28131-z

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Scientific Reports (2023)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.